Interdiffusion Behavior of Aluminide Coated Two-Phase α2-Ti3Al/γ-TiAl Alloys at High Temperatures
DOI:
https://doi.org/10.5614/j.eng.technol.sci.2016.48.5.3Abstract
Lower density materials of TiAl based intermetallic alloys have recently attracted intensive attention for the replacement of nickel-based superalloys used at high temperatures. As aluminium-rich titanium aluminide intermetallic compounds are normally brittle, two-phase α2-Ti3Al/γ-TiAl alloys have been developed. To increase the corrosion resistance of these alloy systems, an aluminide coating of TiAl3 layer is normally applied. During operation at high temperatures, however, interdiffusion between the coating and the alloy substrate can occur and decrease the TiAl3 layer thickness of the coating. The effects of temperature exposure on the growth of the TiAl2 interdiffusion zone layer on two-phase α2-Ti3Al/γ-TiAl alloys with a chemical composition of Ti-47Al-2Nb-2Cr-0.5Y-0.5Zr are presented in this paper. The exponents for kinetics and rate constant of the TiAl2 interdiffusion layer growth of this multi-component system were found under variation of temperature. The results were compared with those from other researchers.Downloads
References
Van de Voorde, M.H., Protective Coatings for Materials in High Temperature Technology, Surface Engineering, Surface Modification of Materials, Kossowsky, R., and Singhal, S.C. (eds.), Nijhoff Publishers, Boston, United States, pp. 390-417, 1984.
Streiff, R., Protection of Materials by Advanced High Temperature Coatings, Colloque C9, Supplement au Journal de Physique III, 3, pp. 17-41, 1993.
Xiang, Z.D., Ros, S. & Datta, P.K., Pack Deposition of Coherent Aluminide Coatings on -TiAl for Enhancing Its High Temperature Oxidation Resistance, Surface and Coating Technology, 161(2-3), pp. 286-292, 2002.
Tang, Z., Niewolak, L, Shemet, V., Singheiser, L., Quadakkers, W.J., Wang, F., Wu, W. & Gil, A., Development of Oxidation Resistant Coatings for -TiAl Based Alloys, Materials Science and Engineering: A, 328(1-2), pp. 297-301, 2002.
Basuki, E., Prajitno, D. & Pawawoi, Oxidation Behavior of Aluminide Coated Ti-Al-Cr-Nb-Zr-Y Alloys at High Temperatures, Solid State Phenomena, 227, pp. 343-348, 2015.
Murray, J. L., Al-Ti (Aluminum-Titanium), ASM Handbook, Volume 3, Alloy Phase Diagrams, ASM International, p. 327, 1998.
Basuki, E., Mohammad, F., Fauzi, A., & Prajitno, D., Hot Corrosion of Aluminide Coated Ti-Al-Cr-Nb-Zr-Y Intermetallic Alloys, Advanced Materials Research, 1112, pp. 363-366, 2015.
Muhammad, F., Basuki, E.A. & Juliansyah, M.I., The Interdiffuison Modeling of Aluminide Coated Ti-47Al-2Cr-2Nb-0.5Zr-0.5Y, Indonesian Journal of Physics, 26(1), July, pp. 13-16, 2015.
Van Loo, F.J.J. & Rieck, G.D., Diffusion in Titanium-Aluminium System - I: Interdiffusion Between Solid Al and Ti or Ti-Al Alloys, Acta Metallurgica, 21(1), pp. 61-71, 1973.
Chu, M.S. & Wu, S.K., Interreactions of TiAl3 Thin Film on Bulk -TiAl and on Bulk 2-Ti3Al Alloys at 700-1000 C, Materials Transactions, 45(4), pp. 1290-1298, 2004.
Xu, L., Cui, Y.Y., Hao, Y.L. & Yang, R., Growth of Intermetallic Layer in Multi-laminated Ti/Al Diffusion Couples, Materials Science and Engineering A, 435-436, pp. 638-647, 2006.
Kirkaldy, J.S. & Young, D.J., Diffusion in the Condensed State, The Institute of Metals, pp. 127-147, 1987.
Gschneidner, K.A. & Kalderwood, F.W., Al-Y (Aluminum-Ytrrium), ASM Handbook, Volume 3, Alloy Phase Diagrams, ASM International, p. 333, 1998.
Wagner, C., The Evaluation of Data Obtained with Diffusion Couples of Binary Single-phase and Multiphase Systems, Acta Metallurgica, 17(2), pp. 99-107, 1969.