Study on the Making of Blended Cement by Mixing Granulated Blast Furnace Slag with Portland Cement Clinker
Keywords:
cement hydration, compressive strength fineness, granulated blast furnace, portland cement clinker, slag, hidrasi semen, kehalusan, klinker semen Portland, kuat tekan, terak tanur tiupAbstract
Abstract. This paper presents the results of laboratory into the effect of slag fineness and slag composition added to portland cement clinker, to the compressive strength of the paste. The results showed that slag of 4260 cm2/gram fineness can be added up to 3O% to a portland cement clinker to increase compressive strength from 28 MPa to about 40 MPa. Scanning electron micrograph of the pastes showed that the inter granular voids between slag particles and sand particles were densely filled with line CaO-SiO2-H2O gel after 28 days observation, and in case clinker without slag, densification of CaO-SiO2-H2O gel still left pores even after 23 days of observation. The fineness of slag is more important than its composition in the blended cement.
Studi Pembuatan Semen Campur (Blended Cement) dari Campuran Terak Tanur Tiup dan Klinker Semen Portland
Sari. Paper ini menyajikan hasil percobaan laboratorium yang meneliti pengeruh kehalusan terak dan komposisi terak yang ditambahkan ke dalam klinker semen Portland. Hasil percobaan menunjukkan bahwa terak dengan kehalusan 4260 cm2/gram dapat ditambahkan ke dalam klinker sampai maksimum 30%, untuk meningkatkan kuat tekan dari semula 28 Mpa menjadi 40 Mpa. Foro SEM menunjukkan bahwa kekosongan antarbutir partikel terak dengan partikel pasir terisi dengan baik oleh pasta halus CaO-SiO2-H2O setelah pengamatan selama 28 hari. Untuk klinker tanpa terak, pasta masih mempunyai pori mesipun setelah 28 hari pengamatan. Kehalusan terak lebih penting daripada komposisinya di dalam semen campur.
References
Ashed, H., "Kontibusi Nikel Slag-Cement terhadap kekuatan dan durabilitas beton kinerja tinggi" , Thesis, Magister Rekayasa Struktur, Teknik Sipil, ITB, 1998.
Frigione, G., and Sersale, R., "Blast furnace cement mortart manufactured with fresh granulated and weathed slags" , Cement and Concrete Research, 24, 3,(1987).
Kosasih, K.M., "Studi pemanfaatan terak tanur tiup sebagai bahan substitusi parsial klinker dalam pembuatan semen Portland pozzolan" , Tugas Akhir, Jurusan Teknik Pertambangan, FIKRM, ITB, 1999.
Lea, F. M., "The Chemistry of cement and concrete" . London, 1970.
Sudarsono, A., and Zamani, A., "Study on the making of blended cement by mixing slag with ordinary Portland cement type I" ,(in preparation).
Zamani, A., "Studi pembuatan semen pozzolan portland dari campuran terak tanur tiup dengan semen portland tipe I" , Tugas Akhir, Jurusan Teknik Pertambangan, FIKTM, ITB, 1999.